Synergy Polymers :: ABS Glass Filled

	Product Characteristics / Applications
	Properties
	Process Parameters

Back

Product Characteristics / Applications
ABS Glass Filled
Grade	Description	Features	Applications
AGR15	ABS Glass Filled 15%	Reduced shrinkage, Good mechanical and thermal properties, Good Surface Finish, Special property enhancement for resistant to wear	Textile pulleys, and machine parts, Airconditioner fans, Impellers, Brackets, Motor casing, Meter housing.
AGR30	ABS Glass Filled 30%

Top

Properties
ABS Glass Filled
PROPERTY	ASTM METHOD	UNITS	AGR15	AGR30
Specific gravity	D - 792		1.05	1.3
Mould shrinkage (Along the flow on 3mm thickness)	D - 955	%	0.30-0.70	0.20-0.30
Tensile strength	D - 638	MPa	82	88
Elongation at break	D - 638	%	10.5	8.5
Flexural strength	D - 790	MPa	96	103
Flexural Modulus	D - 790	MPa	5500	6100
Izod impact strength	D - 256 A	Kg.cm/cm	8*	7.5*
Heat Deflection Temperature	D - 648
'@ 18.5 kg/sq.cm load		Deg.C	96	100
'@ 4.6 kg/sq.cm load		Deg.C	99	104

* Values obtained on conditioned test specimens. Properties measured on natural grades under Dry-as-moulded test specimens and standard testing conditions. Pigmented grades would record slightly lower mechanical properties as permitted by ASTM D-4066.
Information given here is to the best of our knowledge and experience, provided in good faith but Synergy assumes no liability and no warrant is attached. The user assumes all responsibility for the use of all information provided and shall verify quality

Top

ABS

Process Parameters

Glass Filled

Product

Feed Zone Temperature

Compression Zone Temperature

Metering Zone Temperature

Nozzle Temperature

Melt Temperature

Injection Pressure Kg/Cm2

Mould Temperature

AGR15

195

210

225

210

205

1150

AGR30

210

225

230

215

1250

Injection pressure : The above given values or as sufficient to fill cavities.

Conditioning : It is advised to condition components in hot water at 80-100 Deg. C for 2 – 4 hrs. depending upon the component thickness and as required by the subsequent process also to release internal stresses if any to avoid breakage during further assemply.

Above parameters are only guidelines and exact process conditions have to be established for each machine/mould depending upon equipment capacity, part geometry. It is given in good faith and no warrant is attached.

Top