Synergy Polymers :: SAN Glass Filled

	Product Characteristics / Applications
	Properties
	Process Parameters

Back

Product Characteristics / Applications
SAN Glass Filled
Grade	Description	Features	Applications
SANGR20	SAN Glass Filled 20%	Excellent dimensional stability, Good impact strength, (for impact modified grades), High creep resistance and chemical resistance	Battery Cases, Window Panel, Speedometer Cover, Instrumental Panels, Terminal Box, instrument lenses, appliance knobs

Top

Properties
SAN Glass Filled
PROPERTY	ASTM METHOD	UNITS	SANGR20
Specific gravity	D - 792		1.22
Mould shrinkage (Along the flow on 3mm thickness)	D - 955	%	0.10-0.30
Tensile strength	D - 638	MPa	105
Elongation at break	D - 638	%	6.5
Flexural strength	D - 790	MPa	155
Flexural Modulus	D - 790	MPa	6300
Izod impact strength	D - 256 A	Kg.cm/cm	4*
Heat Deflection Temperature	D - 648
'@ 18.5 kg/sq.cm load		Deg.C	110
'@ 4.6 kg/sq.cm load		Deg.C	120

* Values obtained on conditioned test specimens. Properties measured on natural grades under Dry-as-moulded test specimens and standard testing conditions. Pigmented grades would record slightly lower mechanical properties as permitted by ASTM D-4066.
Information given here is to the best of our knowledge and experience, provided in good faith but Synergy assumes no liability and no warrant is attached. The user assumes all responsibility for the use of all information provided and shall verify quality

Top

SAN

Process Parameters

Glass Filled

Product

Feed Zone Temperature

Compression Zone Temperature

Metering Zone Temperature

Nozzle Temperature

Melt Temperature

Injection Pressure Kg/Cm2

Mould Temperature

SANGR20

200

220

230

220

210

1250

Injection pressure : The above given values or as sufficient to fill cavities.

Conditioning : It is advised to condition components in hot water at 80-100 Deg. C for 2 – 4 hrs. depending upon the component thickness and as required by the subsequent process also to release internal stresses if any to avoid breakage during further assemply.

Above parameters are only guidelines and exact process conditions have to be established for each machine/mould depending upon equipment capacity, part geometry. It is given in good faith and no warrant is attached.

Top

Back